Effect of Surface Quality of Titanium Plate on the Interface between Titanium and Steel Plates

摘要: 通过测试爆炸钛-钢复合板结合强度和分析钛板表面质量情况,研究了复合板中钛层产生分层、碎边和皱褶缺陷的原因。结果表明,钛板上残留的冶金缺陷、板形不良和不均匀的边部致密氧化层残留,会造成复合板界面的结合不牢。针对复合时界面结合不牢的问题,提出了对钛板的质量管控和表面处理的适宜措施。
- 表面质量 /
- 钛-钢复合板 /
- 氧化层 /
- 界面结合
Abstract: To find out the reasons for the delamination, broken edge and folds of the Ti plate, the bonding strength of the explosive welding Ti-steel clad plate is tested, and the surface quality of the Ti plate is analyzed. The results shows that the metallurgical defect of Ti ingot, broken edge and heterogeneous oxidation layer contribute to the weak bonding of the clad plates. Then, the suitable measures for the quality control and surface treatment of the Ti plate are put forward.
- surface quality /
- Ti-steel clad plate /
- oxidation layer /
- interface bonding

[1]	宋磊, 邹见宾, 李松元, 等. 钛/钢爆炸复合板边界效应的产生与预防[J]. 有色金属工程, 2015, 5(2):1-3.
[2]	王小华. 电厂烟囱用钛-钢复合板钛复材焊接缺陷产生原因及预防措施[J]. 材料开发与应用, 2012, 27(4):102-105.
[3]	辛宝, 岳宗洪, 邓光平, 等. 钛-钢复合板热轧工艺研究[J]. 材料开发与应用, 2016, 31(6):75-79.
[4]	国家质量监督检验检疫总局, 中国国家标准化管理委员会. 钛-钢复合板:GB/T 8547-2006[S]. 北京:中国标准出版社, 2006.
[5]	王飞, 刘广初, 王连来. 减小爆炸焊接边界效应影响研究[J]. 工程爆破, 2005, 11(2):6-9.
[6]	辛宝, 刘金涛, 崔卫超, 等. 钛的屈服强度对大面积钛-钢复合板结合性能的影响[J]. 材料开发与应用, 2015, 30(6):10-14.