Property of Cu-Al Functional Gradient Material

  • The purpose of the study is to solve the problem of burnout and electric shocking of copper and aluminum joints in high-current equipment.Copper/aluminum functional gradient material samples were prepared by powder overlaying.It was found that the seven lays sample sintered at 620℃ has higher hardness and lower resistivity,of which the joints of copper/aluminum wire could be made.θ(CuAl2) generated in sintered samples dilution zone and hardness in local area increased notablely.The resistivity of samples sintered at 540℃ is the lowest.As the sintering temperature increased,liquid sintering happened and the sintering perfomed more sufficient,so the content of θ(CuAl2) and then average hardness and the resistivity increased.
  • loading

Catalog

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return