LI Xue-feng, WANG Chun-fen. Analysis on Crack of Roll Axis[J]. Development and Application of Materials, 2012, 27(2): 73-76. DOI: 10.19515/j.cnki.1003-1545.2012.02.017
Citation:
LI Xue-feng, WANG Chun-fen. Analysis on Crack of Roll Axis[J]. Development and Application of Materials, 2012, 27(2): 73-76. DOI: 10.19515/j.cnki.1003-1545.2012.02.017
LI Xue-feng, WANG Chun-fen. Analysis on Crack of Roll Axis[J]. Development and Application of Materials, 2012, 27(2): 73-76. DOI: 10.19515/j.cnki.1003-1545.2012.02.017
Citation:
LI Xue-feng, WANG Chun-fen. Analysis on Crack of Roll Axis[J]. Development and Application of Materials, 2012, 27(2): 73-76. DOI: 10.19515/j.cnki.1003-1545.2012.02.017
The fracture of roll axis was synthetically analyzed by means of macroscopic test,EDS and optical microscopy and other ways.The results showed that the fatigue failures of the roll axis was arised from the hydrogen induced cracking.