ZHANG Haifeng, LI Xuefeng, ZHANG Yonghui. Failure Analysis of Cracking of Nut[J]. Development and Application of Materials, 2013, 28(1): 72-75. DOI: 10.19515/j.cnki.1003-1545.2013.01.016
Citation:
ZHANG Haifeng, LI Xuefeng, ZHANG Yonghui. Failure Analysis of Cracking of Nut[J]. Development and Application of Materials, 2013, 28(1): 72-75. DOI: 10.19515/j.cnki.1003-1545.2013.01.016
ZHANG Haifeng, LI Xuefeng, ZHANG Yonghui. Failure Analysis of Cracking of Nut[J]. Development and Application of Materials, 2013, 28(1): 72-75. DOI: 10.19515/j.cnki.1003-1545.2013.01.016
Citation:
ZHANG Haifeng, LI Xuefeng, ZHANG Yonghui. Failure Analysis of Cracking of Nut[J]. Development and Application of Materials, 2013, 28(1): 72-75. DOI: 10.19515/j.cnki.1003-1545.2013.01.016
For the craching of a titanium nut occured in working process,chemical analysis,metallurgical structure inspection and microstructure observation were conducted.The results revealed that the cracking of the nut was originated from stress corrosion.