Research on Matching and Antifouling Performance of Zinc Acrylate Self-polishing Antifouling Paint

Polishing antifouling coating was prepared with zinc acrylate resin as base material, and the adhesion between the selfpolishing antifouling coating and the tie paint and the properties of self-polishing and antifouling were studied.Resultsshow that the adhesive force of the tie coating and antifouling coating is up to 2 MPa, and the crack occurs cohesively in the antifouling coating, showing great adhesion between the coatings. Erosion rate test result shows that the polishing rate stabilizes at 65 μm/a.Submerged in the shallow sea for 3 years, the antifouling coating on the panels is almost clean of marine fouling organisms, which shows antifouling performance of the coating is good.