Study on Properties of Epoxy Resin Curing System for Marine Concrete Structures

More Information
  • Received Date: May 22, 2022
  • Available Online: March 10, 2023
  • With the rapid development of marine economy, the demand for marine concrete structure corrosion repairing and reinforcement technology is increasing. The existing repair technology of concrete structures above ground level is very mature. The applicability of epoxy resin curing system to the marine environment is the key issue to expand its application environment from the ground surface engineering to the offshore engineering. In this paper, 7 kinds of commercial curing agents are selected and screened by curing agent, viscosity of resin system and underwater gel time. The effects of curing environment and time and dosage of curing agent on compression properties of the resin system are studied. Finally, through the study of tensile properties and bond properties, it is concluded that the 810 curing agent has the best comprehensive performance in seawater environment. The results show that when the mass ratio of the epoxy resin E51 to the curing agent 810 is 2∶1, the epoxy resin is placed in seawater cured for 7 d, and the underwater gel time is 65 min, the compressive strength of the epoxy resin is 101.59 MPa, the tensile strength 32.59 MPa, the elongation at break 4.09%, and the bond strength 3.52 MPa.
  • [1]
    侯保荣.海洋钢筋混凝土腐蚀与修复补强技术[M].北京:科学出版社, 2012:9-19.
    [2]
    王卫军.水下环氧树脂固化剂在水利工程应用中的技术与性能[J].粘接, 2019, 40(12):5-8.
    [3]
    廖婉蓉,张贵金,肖通,等.一种适合混凝土水下修复的新型环氧砂浆[J].长江科学院院报, 2019, 36(2):127-131.
  • Cited by

    Periodical cited type(2)

    1. 黄丹蓉,颜龙,李昀,徐志胜. 环氧树脂/聚酰胺配比对膨胀型钢结构防火涂料防火和抑烟性能的影响. 涂料工业. 2024(03): 8-14 .
    2. 张晨,李笑甜,丁明惠,朱怀清,明丽君,刘欣雨. PhN-DOPO改性环氧树脂的制备及性能. 精细化工. 2024(11): 2522-2530 .

    Other cited types(0)

Catalog

    Article Metrics

    Article views (273) PDF downloads (22) Cited by(2)
    Related

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return