船用ZG14CrNi3MoV铸钢两相区热处理工艺研究

Research on Two-phase Region Heat Treatment of ZG14CrNi3MoV Marine Cast Steel

摘要: 对比了"单相区淬火+两相区淬火+高温回火"和"单相区保温+缓冷进入两相区+高温回火"和"两相区直接淬火+高温回火"3种热处理工艺对船用ZG14CrNi3MoV铸钢显微组织和力学性能的影响。结果表明,ZG14CrNi3MoV铸钢采用"单相区淬火+两相区淬火+高温回火"工艺进行热处理后,组织为铁素体+回火索氏体混合组织,强韧性匹配良好。
- 铸钢 /
- 两相区 /
- 屈服强度 /
- 低温韧性
Abstract: The effects of three heat treatment processes of the ZG14CrNi3MoV cast steel microstructure and mechanical properties were compared, which were "single-phase zone quenching+two-phase zone quenching+high temperature tempering", "single-phase zone insulation+slow cooling into two-phase zone+high temperature tempering", "two-phase zone quenching+high temperature tempering". The results show that the two-phase zone heat treatment process has a great influence on the microstructure and mechanical properties of ZG14CrNi3MoV cast steel. The heat treatment process of "single-phase zone quenching+two-phase zone quenching+high temperature tempering" is adopted. The microstructure of cast steel is ferrite and tempered sorbite, and the strength and toughness match well.
- cast steel /
- two-phase region /
- yield strength /
- low temperature toughness

[1]	罗小兵, 杨才福, 柴锋, 等. 两相区二次淬火对高强度船体钢低温韧性的影响[J]. 金属热处理, 2012, 37(9): 71-74.
[2]	肖纪美. 金属的韧性与韧化[M]. 上海: 上海科学技术出版社, 1980.
[3]	张怀征, 刘东升. 热处理工艺对高强度含铜9Ni钢组织和性能的影响[J]. 钢铁, 2011, 46(7): 79-85.
[4]	蒋春宏, 余崎宇, 马勤. 热处理对大截面LS8铸钢组织和性能的影响[J]. 金属热处理, 2015, 40(4): 77-81.
[5]	王祖华, 杨超飞, 牛继承, 等. 两相区热处理对ZG14Ni3CrMoV铸钢低温韧性的影响[J]. 材料开发与应用, 2017, 32(4): 5-8.