Research on Thermal Aging Performance of Damping Composites
-
摘要: 结构阻尼复合材料具有高比强度、高比模量、高阻尼等特性,用于船舶领域具有减振降噪的优良特性。为了研究结构阻尼复合材料在热环境下性能演变规律,本研究以玻纤复合材料及共固化阻尼改性的结构阻尼复合材料为研究对象,开展了结构阻尼复合材料力学性能、阻尼性能,及其耐湿热老化性能研究。研究发现:经阻尼处理后,复合材料的阻尼性能提高了1倍;短时热老化试验,对阻尼复合材料的力学和阻尼性能影响较小;通过长期热老化试验并根据阿伦尼乌斯方程,建立了结构阻尼复合材料的寿命方程,并推算出其最高使用温度为82.1℃,满足预期使用需求。Abstract: The damping composites are fabricated with glass fiber, viscoelastic layer and epoxy resin via VARI co-curing process. It exhibits high strength, rigidity, loss factor and good heat distortion temperature. Different kinds of thermal aging test are conducted on the damping composites. The results indicates that the mechanical properties and damping properties are less affected after the short-term thermal aging tests. Meanwhile, the lifetime equation is established according to the performance evolution of the damping composites during the accelerated aging test, and the maximum service temperature is 82.1℃.
-
Key words:
- damping composites /
- loss factor /
- flexural performance /
- thermal aging performance
-
[1] 秦天腾, 丁永乐, 郭君, 等. 复合材料铺层角度对螺旋桨受力特性影响分析[J]. 舰船科学技术, 2023, 45(8):20-25. [2] 吕林华, 杨德庆. 船舶钢-复合材料组合基座减振设计方法分析[J]. 上海交通大学学报, 2012, 46(8):1196-1202. [3] 余启勇, 马玉璞, 郭万涛, 等. 结构阻尼复合材料及其研究进展[J]. 材料工程, 2007, 35(S1):253-258. [4] 高影. 纤维增强树脂基复合材料及其结构的阻尼性能研究[D]. 哈尔滨:哈尔滨工业大学. [5] 倪楠楠,温月芳,贺德龙, 等. 结构-阻尼复合材料研究进展[J]. 材料与工程,2015,43(6):90-101. [6] 杨霜, 孙康, 吴人洁. 混杂纤维复合材料阻尼性能的研究[J]. 纤维复合材料, 2002, 19(1):6-10. [7] 邱磊, 陈友恒, 宋金鹏, 等. 碳玻混杂复合材料阻尼性能研究[J]. 材料开发与应用, 2020, 35(6):84-87. [8] 张少辉, 陈花玲. 共固化复合材料粘弹阻尼结构的损耗因子研究[J]. 航空材料学报, 2005, 25(1):53-57. [9] 潘利剑, 张博明, 戴福洪. 粘弹阻尼层共固化复合材料的阻尼特征分析[J]. 振动与冲击, 2009, 28(4):10-13. [10] 何纯磊, 于运花, 李晓超, 等. 碳纤维/环氧树脂复合材料加速热氧老化研究[J]. 玻璃钢/复合材料, 2012(2):25-29. [11] 董安琪, 段跃新, 肇研, 等. 湿热环境对PMI泡沫夹芯复合材料性能的影响[J]. 复合材料学报, 2012, 29(2):46-52. [12] 潘利剑, 张博明, 戴福洪. 黏弹阻尼层共固化复合材料不同温度下的阻尼性能[J]. 复合材料学报, 2008, 25(1):168-172. [13] 过梅丽. 高聚物与复合材料的动态力学热分析[M]. 北京:化学工业出版社, 2002. -
点击查看大图
计量
- 文章访问数: 51
- HTML全文浏览量: 8
- PDF下载量: 11
- 被引次数: 0
下载: