热处理工艺对二氧化锡雾化粉粒度及均匀性的影响

Effect of Heat Treatment Process on Particle Size and Uniformity of SnO₂ Atomized Powder

摘要: 以Sn为原料采用电弧等离子雾化工艺制备出四方相未完全氧化的纳米二氧化锡粉末，在空气气氛条件下，研究采用不同热处理工艺，氧化锡粉末生长速率与温度的关系。采用不同热处理温度和保温时间的热处理工艺对原始氧化锡粉末进行了热处理。采用X射线衍射（XRD）、扫描电子显微镜（SEM）等方法对样品进行了成分和形貌分析。试验结果表明，采用等离子雾化法制备的氧化锡粉末，其晶粒尺寸随温度呈两段式增长，合适的热处理工艺可以改善粉末的粒度均匀性。
- 二氧化锡 /
- 纳米 /
- 热处理
Abstract: Incomplete oxidation nano SnO₂ powder with tetragonal phase was prepared by arc plasma process with Sn as raw material. The relationship between the growth rate and the temperature of SnO₂ powder was studied by different heat treatment process. The original SnO₂ powder was heat treated with different temperatures and holding time. X-ray diffraction(XRD) and scanning electron microscope(SEM) were used to analyze the compositions and morphologies of the samples. The experimental results showed that the grain size of SnO₂ powder prepared by plasma atomization increased in two stages with temperature, and the proper heat treatment process could improve the particle size uniformity.
- SnO₂ /
- nanometer /
- heat treatment

[1]	吕逵弟,余林,吴雅红,等.二氧化锡超细粉体的制备及研究进展[J].无机盐工业,2005,37(4):7-11.
[2]	孙姗.二氧化锡粉体的制备研究[D].沈阳:东北大学,2013.
[3]	苗鸿雁,丁常胜,罗宏杰,等.水热合成Sb-SnO₂纳米粉体制备工艺参数的研究[J].稀有金属材料与工程,2003,32(9):761-764.
[4]	王迪,田均庆,张书涛,等.溶胶凝胶法制备二氧化锡纳米晶体[J].哈尔滨商业大学学报(自然科学版),2014,30(2):224-228.
[5]	张晓顺,邱竹贤,翟秀静,等.超声波-化学沉淀法制备纳米二氧化锡[J].东北大学学报,2005,26(4):265-267.
[6]	谢斌,张秀勤,赵福辰,等.基于TRIZ改善微米氧化锡粉末粒度均匀性[J].材料开发与应用,2019,34(4):98-102.
[7]	戴遐明,艾德生,李庆丰.纳米ZrO₂粉体的热处理研究[J].中国粉体技术,2001,7(5):10-14.
[8]	王欣,魏宗平,唐电.热处理对活性氧化物晶粒尺寸的影响[J].材料热处理学报,2010,31(11):7-11.
[9]	李青山,张金朝,宋鹂.热处理对掺锑二氧化锡纳米导电粉粒度和性能的影响[J].无机材料学报,2002,17(3):489-496.
[10]	梁镇海,张文涛,张业.Sn₁-_x-_yMn_xSb_yO₂体系固溶体的相关系及形成机制[J].人工晶体学报,2011,40(1):181-186.