Study on the Influence Factors of Leakage Current of Tantalum Wires for Capacitors
-
摘要: 研究了钽丝的纯度、漏电流检测条件对钽丝漏电流的影响。结果表明，钽丝中化学杂质的含量对钽丝漏电流的影响尤为明显，而合适配比的掺杂剂和掺杂量可以显著降低钽丝的漏电流；钽丝的阳极氧化条件也是影响漏电流的重要因素。可以通过控制钽丝的纯度、优化阳极氧化形成条件，获得稳定、可靠的钽丝漏电流。Abstract: The effects of the tantalum wire purity and leakage current test conditions analysis on the tantalum wire leakage current were studied.Resultsshowed that the appropriate content of doping agent and the suitable ratio could significantly reduce the leakage current of tantalum wire. The anodic oxidation condition of tantalum wire was also an important factor affecting the leakage current. By controlling the purity of tantalum wire and optimizing anodizing conditions, the stable and reliable tantalum wire leakage current could be obtained.
-
Key words:
- tantalum wire /
- doping /
- anodic oxidation /
- leakage current
-
[1] 许宁辉.阴极比表面积对超高比容钽阳极容量测试结果的影响[J].宁夏工程技术,2013,12(3):267-269. [2] 万庆峰,田苗,陈林,等.掺杂元素Ge和Ce及掺杂量对钽丝组织和性能的影响[J].材料热处理学报,2013,34(9):127-131. [3] 黄伯云.中国材料工程大典[M].北京:化学工业出版社,2005:247-250. [4] 吴铭,邵志俊,孙有路.钽铌冶金工艺学[M].北京:中国有色金属工业总公司,1995:309. [5] 万庆峰,王德志,赵兵,等.掺杂锗和铈对钽丝组织和力学性能的影响[J].材料热处理学报,2009,30(1):80-83. [6] 石绪忠,陈派明,王岳,等.5A06铝合金阳极氧化和微弧氧化膜绝缘性能研究[J].材料开发与应用,2012,27(1):51-55. [7] 陈梦华,丰震河,黄英,等.超级电容器电极材料的研究进展[J].材料开发与应用,2018,33(3):90-103. [8] 李仲香,郑金凤,张健康,等.影响电容器钽阳极漏电流因素分析[J].宁夏工程技术,2010,9(2):108-110. [9] 王卫东,陈伟强.固体钽电解电容器漏电流的研究[J].现代测量与实验室管理,2010(5):13-15. [10] 许宁辉,刘军,魏春霞.阳极氧化形成工艺对一氧化铌电性能的影响[J].粉末冶金工业,2019(6):23-26. [11] 万庆峰,王德志,田苗,等.掺杂对钽丝电性能影响的研究[J].电子元件与材料,2008,27(3):39-41. [12] 谢永旭,万庆峰,马跃忠,等.钇掺杂钽丝拉拔断裂机理分析[J].有色金属工程,2014,4(1):24-26. [13] 常亮亮.钛酸锶掺杂改性研究进展[J].材料开发与应用,2014,29(1):89-93. [14] 冒佳卫.阳极氧化及封孔处理对2024铝合金耐腐蚀性能的影响[D].南京:南京邮电大学,2018. -
点击查看大图
计量
- 文章访问数: 50
- HTML全文浏览量: 12
- PDF下载量: 8
- 被引次数: 0
下载: