铜合金垫片表面类金刚石薄膜的制备及其摩擦学性能研究

罗焱泽; 段天应; 李志强; 王永欣

铜合金垫片表面类金刚石薄膜的制备及其摩擦学性能研究

1. 中国船舶重工集团公司第七二五研究所, 河南洛阳 471023;
2. 中国科学院宁波材料技术与工程研究所, 中国科学院海洋新材料与应用技术重点实验室, 浙江省海洋材料与防护技术重点实验室, 浙江宁波 315201

详细信息

作者简介:
罗焱泽,男,1985年生,工程师,主要从事特种金属压力管道元件应用技术研究

中图分类号: TG174.444
计量
- 文章访问数: 177
- HTML全文浏览量: 55
- PDF下载量: 11
- 被引次数: 0
出版历程
- 收稿日期: 2020-06-22
- 刊出日期: 2021-04-25

Fabrication and Tribological Properties of Diamond-Like Carbon Film on Copper Alloy Gasket

1. Luoyang Ship Material Research Institute, Luoyang 471023, China;
2. Key Laboratory of Marine Materials and Related Technologies, Zhejiang Key Laboratory of Marine Materials and Protective Technologies, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201, China

摘要

摘要: 采用物理气相沉积工艺在黄铜H62垫片上制备了DLC薄膜，对DLC薄膜进行了拉曼光谱分析和截面形貌观察，测试了薄膜厚度、纳米硬度和结合力，进行了磨擦磨损试验，分析了薄膜的减摩耐磨性能。结果表明，在H62铜合金垫片制备碳膜为DLC薄膜，薄膜总厚约2.31μm，底层厚约0.49μm。薄膜纳米硬度22.1 GPa，薄膜与基体结合良好，结合性能HF1级，结合力41.1 N。H62铜合金垫片制备DLC薄膜后，摩擦系数由0.55降至0.25，磨损率由1.3×10^-4 mm³/Nm降至1.1×10^-5 mm³/Nm，具有优异的减磨性能和耐磨损性能。装拆10次后，垫片表面DLC薄膜完整，基本无损伤，满足使用要求。
- 黄铜垫片 /
- DLC薄膜 /
- 减摩耐磨性能
Abstract: DLC film was fabricated on the H62 brass gasket by physical vapor deposition. Raman spectroscopy and cross-sectional morphology observation were performed on the film, and the thickness, nanohardness and adhesion strength were tested. Finally, friction-reduction and wear-resistant properties of the DLC film were analyzed after tribological test.Resultsshowed that the thickness of the DLC film on H62 brass gasket was totally 2.31 μm, the thickness of interlayer was approximately 0.49 μm. The hardness of DLC film was 22.1 GPa, and the adhesion between DLC film and the substrate was strong(HF1 for indentation and 41.1 N for scratching). When the H62 brass gasket was coated by DLC film, the friction coefficient decreased from 0.55 to 0.25, the wear rate decreased from 1.3×10^-4 mm³/Nm to 1.1×10^-5 mm³/Nm, meaning good friction-reduction and wear-resistant properties were achieved. After 10 times assembling and disassembling, the DLC film on gasket was complete, and no significant damage could be detected, therefore, the gasket with film could meet the requirement.
- brass gasket /
- DLC film /
- friction-reduction and wear-resistant properties

HTML全文

参考文献(11)

[1]	福伟,张铎,黄国兴.高强耐磨锰黄铜的研究[J].理化检验-物理分册,2006,42(8):389-391.
[2]	国占玲.黄铜的成分、性能及典型应用[J].科学技术与创新,2012(28):66-66.
[3]	陈一胜,傅政,朱志云,等.高强耐磨黄铜的研究现状[J].有色金属科学与工程,2012,3(5):23-29.
[4]	AZZI M,PAQUETTE M,SZPUNAR J A,et al.Tribocorrosion behaviour of DLC-coated 316L stainless steel[J].Wear,2009,267(5):860-866.
[5]	BUENO A H S,SOLIS J,ZHAO H,et al.Tribocorrosion evaluation of hydrogenated and silicon DLC coatings on carbon steel for use in valves,pistons and pumps in oil and gas industry[J].Wear,2018,394-395:60-70.
[6]	YAMAUCHI N,OKAMOTO A,TUKAHARA H,et al.Friction and wear of DLC films on 304 austenitic stainless steel in corrosive solutions[J].Surface and Coatings Technology,2003,174-175:465-469.
[7]	YE Y W,WANG Y X,MA X L,et al.Tribocorrosion behaviors of multilayer PVD DLC coated 304L stainless steel in seawater[J].Diamond and Related Materials,2017,79:70-78.
[8]	苟成学,王顺花,尚伦霖,等:类金刚石薄膜在腐蚀介质中的摩擦磨损行为研究[J].表面技术,2019,48(10):172-179.
[9]	DONNET C,ERDEMIR A.Tribology of diamond-like carbon films:fundamentals and applications[M].New York:Springer,2008.
[10]	薛群基,王立平.类金刚石碳基薄膜材料[M].北京:科学出版社,2012.
[11]	雍青松,王海斗,徐滨士,等.类金刚石薄膜摩擦机理及其摩擦学性能影响因素的研究现状[J].机械工程学报,2016,52(11):95-107.