Effect of Heat Treatment Temperature on Microstructure and Properties of T2+Q345R Composite Plate by Explosive Welding
-
摘要: 研究了热处理对爆炸焊接T2+Q345R复合板组织和性能的影响。结果表明,热处理温度对T2+Q345R复合板的剪切、拉脱、伸长率等影响不明显,650℃以下,复层晶粒度增长缓慢,界面处异种金相组织厚度较爆炸态变化不大;650℃以上,随温度升高,复层晶粒度急剧增长,界面处异种金相组织厚度较爆炸态快速增加。Abstract: The heat treatment experiments have been carried out on T2 and Q345R explosive welding composite plate at series temperatures, and the changes of its structure and properties are observed. The results show that the heat treatment temperature has no obvious effect on the shear strength, tensile strength and elongation of T2-Q345 clad plate. When the temperature is below 600℃, the clad grain size grows slowly, and the thickness of heterogeneous full-phase microstructure at the interface has little change compared with that of the explosive state. When it is above 600℃, with the increase of temperature, the grain size of clad layer grows rapidly, and the thickness of dissimilar metallographic structure at the interface increases rapidly.
-
Key words:
- explosive welding /
- heat treatment /
- grain size /
- heterogeneous microstructure
-
[1] 余永宁, 杨平, 强文江, 等. 材料科学基础[M]. 北京:高等教育出版社, 2006. [2] 张保奇, 周杰士, 郑明光, 等. 904L+14Cr1MoR(H)复合板的热处理工艺研究[J]. 石油化工腐蚀与防护, 2015, 32(4):12-17. [3] 韩卫光, 余学涛, 孙水珠. 热处理及冷变形程度对LC1100组织性能的影响[J]. 上海有色金属, 2007, 28(2):64-68. [4] 蒋晓博, 刘金涛, 韩刚, 等. 热处理温度对316L/Q370qD(TMCP)复合板组织和性能的影响[J]. 材料开发与应用, 2019, 34(6):10-14. [5] 李珂, 张平, 刘慧娟, 等. 晶粒度对铜点蚀行为的影响[J]. 腐蚀与防护, 2013, 34(11):972-976.
点击查看大图
计量
- 文章访问数: 114
- HTML全文浏览量: 17
- PDF下载量: 12
- 被引次数: 0