溶聚丁苯橡胶分子结构对其声学性能的影响研究

Effect of Molecular Structure of Solution Polymerized Styrene Butadiene Rubber on Acoustic Properties

1. Luoyang Ship Material Research Institute, Luoyang 471023, China;
2. Henan Engineering Technology Center of Vibration and Noise Abatement Materials, Luoyang 471023, China

摘要: 丁苯橡胶(SBR)是常用的水下吸声胶种之一,通过研究溶聚丁苯橡胶(SSBR)分子链中苯乙烯含量和环氧化对其水压下吸声性能的影响,显示SSBR样品吸声系数随测试压力变化不大。在各测试压力下,低苯乙烯含量的SSBR样品吸声性能较差,随着链中苯乙烯含量的提高,吸声性能有明显的改善;极性化改性处理SSBR能够有效提升其加压状态的吸声性能,在极化基团质量分数达到10%时,吸声性能有明显提升。
- 溶聚丁苯橡胶 /
- 分子结构 /
- 吸声性能
Abstract: Styrene butadiene rubber(SBR) is one of the commonly used underwater sound absorption rubber. Here were studied the effects of styrene content and polarizability of SSBR molecular structure on its sound absorption properties. The results of sound absorption test showed that the sound-absorbing performance changed little with the increase of test pressure. The sound absorption performance of SSBR with lower styrene content was poor under various test pressures. With the increase of styrene content in the chain, the sound absorption performance was obviously improved. Polarization modification of SSBR could effectively improve its sound absorption under pressure. When the mass fraction of polarizing group reached 10%, the sound absorption performance was obviously improved.
- SSBR /
- molecular structure /
- sound absorption property

[1]	齐玉霞.溶聚丁苯橡胶改性技术研究进展[J].轮胎工业,2015,35(6):323-327.
[2]	侯永振,王兵.橡胶微观结构因素对声障板吸声性能的影响[J].材料开发与应用,2017,32(4):81-88.
[3]	田珍珍,龚光碧,董静,等.溶聚丁苯橡胶结构与性能关系及其改性方法[J].当代化工,2015,44(11):2638-2641.
[4]	胡昌飞,张聪,张春庆,等.溶聚丁苯橡胶玻璃化转变温度的主要影响因素研究[J].材料开发与应用,2019,34(1):74-79.
[5]	王兵,任伟伟,王雯霏.静压力下粘弹性阻尼材料自由体积分数的分子模拟研究[J].材料开发与应用,2016,31(6):1-5.
[6]	罗开强,罗艳龙,刘昊北,等.链中改性溶聚丁苯橡胶对白炭黑分散性影响的实验研究和分子模拟[J].轮胎工业,2017,37(7):404-409.