环氧粉末涂料的固化机制研究

鲁自界,  李劲,  周钟泉,  贺智端,  张立新,  柯伟

downloadPDF
文章导航 > 材料开发与应用  > 2000 >  15(2): 8-11
鲁自界, 李劲, 周钟泉, 贺智端, 张立新, 柯伟. 环氧粉末涂料的固化机制研究[J]. 材料开发与应用, 2000, 15(2): 8-11. doi: 10.19515/j.cnki.1003-1545.2000.02.003
引用本文: 鲁自界, 李劲, 周钟泉, 贺智端, 张立新, 柯伟. 环氧粉末涂料的固化机制研究[J]. 材料开发与应用, 2000, 15(2): 8-11. doi: 10.19515/j.cnki.1003-1545.2000.02.003
shu
Lu Zijie, Li Jing, Zhou Zhongquan, He Zhiduan, Zhang Lixin, Ke Wei. The Study of Cure Mechanism of a Fusion-bonded Epoxy Powder Coating[J]. Development and Application of Materials, 2000, 15(2): 8-11. doi: 10.19515/j.cnki.1003-1545.2000.02.003
Citation: Lu Zijie, Li Jing, Zhou Zhongquan, He Zhiduan, Zhang Lixin, Ke Wei. The Study of Cure Mechanism of a Fusion-bonded Epoxy Powder Coating[J]. Development and Application of Materials, 2000, 15(2): 8-11. doi: 10.19515/j.cnki.1003-1545.2000.02.003
shu

环氧粉末涂料的固化机制研究

doi: 10.19515/j.cnki.1003-1545.2000.02.003

  • 1. 中国科学院金属腐蚀与防护研究所, 金属腐蚀与防护国家重点实验室 沈阳 110015;

  • 2. 中国科学院长春应用化学研究所 长春 130022

基金项目: 

国家自然科学基金资助课题No.59571060

详细信息
    作者简介:

    鲁自界:男,1973年生,中国科学院金属腐蚀与防护研究所硕士研究生。

  • 中图分类号: TQ630.1

The Study of Cure Mechanism of a Fusion-bonded Epoxy Powder Coating

  • 1. Institute of Corrosion and Protection of Metals, the Chinese Academy of Sciences, Shenyang 110015, China;

  • 2. Institute of Applied Chemistry, the Chinese Academy of Sciences, Changchun 130022, China

    摘要
  • 摘要: 用丁酮作萃取溶剂, 研究了环氧/双氰胺粉末涂层自由膜在160~230℃温度下经不同时间固化后的萃取固化度, 分析了涂膜固化反应的动力学过程。在研究温度范围内, 固化反应表现出单一的表观激活能。环氧/双氰胺粉末涂料的固化反应相当复杂, 既有环氧基与胺基的加成反应, 又有体系中羟基与氰基的聚合反应。文中讨论了固化反应机理, 澄清了两种反应的相对作用。

     

    Abstract: The degree of cure (DOC) of a new type of epoxy/dicyandiamide powder coatings was detected by using solvent extraction on the free film cured at temperatures from 160℃to 230℃ for different time and the kinetic process was analyzed. The results revealed that the cure reaction yielded a single Arrhenius activation energy (91.4kJ/mol), which indicated that there might be only one overall reaction mechanism in the range of the temperature tested. The cure reaction of epoxy/dicyandiamide powder system was complex, involving two principal reactions between epoxide and amine hydrogen, and between hydroxyl groups and —CN. The cure mechanism was also discussed.

     

    • HTML全文
    • 参考文献(0)
    • 相关文章
    • 施引文献
  • 资源附件(0)
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  31
  • HTML全文浏览量:  10
  • PDF下载量:  2
  • 被引次数: 0
出版历程
  • 收稿日期:  1999-08-20
  • 修回日期:  1999-09-27
  • 网络出版日期:  2024-06-17

目录

    /

    返回文章
    返回

    版权所有 © 《材料开发与应用》编辑部豫ICP备13020589号-2

    地址：  电话：(0379)67256265;  (0379)67256345  Email：TG023@163.com

    本系统由 北京仁和汇智信息技术有限公司 开发    百度统计