Influence of Graphite Adding to the Solution of Sodium Hydroxide on the Growth and Wear Resistance of the Coatings Formed by Microarc Oxidation on Aluminum Alloys
-
摘要: 在NaOH溶液中添加石墨粉末后对LY12铝合金进行了微弧氧化处理。分析了石墨相的含量对微弧氧化陶瓷层生长过程的影响和微弧氧化陶瓷层的相组成,在自制的磨损试验机上测定了陶瓷层和对摩件的耐磨损性能。结果表明,石墨相的引入大大降低了陶瓷层以及对摩件的磨损失重。Abstract: The LY12 aluminum alloy was treated in sodium hydroxide solution after adding graphite powder. The influence of the graphite content in the solution on the growth principle and the phase composition of the coating was investigated. The wear resistance of the coatings and the counter was also studied. The results showed that a certain amount of graphite becomed the part of the coatings after oxidation, and this greatly reduced the weight loss of the coatings and the counter.
-