稀土合金钢09Cr2AlMoRE的耐CO2腐蚀性评价

王静,  白真权,  林冠发,  李鹤林

downloadPDF
文章导航 > 材料开发与应用  > 2005 >  20(5): 26-29
王静, 白真权, 林冠发, 李鹤林. 稀土合金钢09Cr2AlMoRE的耐CO2腐蚀性评价[J]. 材料开发与应用, 2005, 20(5): 26-29. doi: 10.19515/j.cnki.1003-1545.2005.05.009
引用本文: 王静, 白真权, 林冠发, 李鹤林. 稀土合金钢09Cr2AlMoRE的耐CO2腐蚀性评价[J]. 材料开发与应用, 2005, 20(5): 26-29. doi: 10.19515/j.cnki.1003-1545.2005.05.009
shu
WANG Jing, BAI Zhen-quan, LIN Guan-fa, LI He-lin. CO2 Corrosion Behavior of 09Cr2AlMoRE Steel[J]. Development and Application of Materials, 2005, 20(5): 26-29. doi: 10.19515/j.cnki.1003-1545.2005.05.009
Citation: WANG Jing, BAI Zhen-quan, LIN Guan-fa, LI He-lin. CO2 Corrosion Behavior of 09Cr2AlMoRE Steel[J]. Development and Application of Materials, 2005, 20(5): 26-29. doi: 10.19515/j.cnki.1003-1545.2005.05.009
shu

稀土合金钢09Cr2AlMoRE的耐CO2腐蚀性评价

doi: 10.19515/j.cnki.1003-1545.2005.05.009

  • 1. 中国石油天然气集团公司石油管力学和环境行为重点实验室, 陕西西安 710065;

  • 2. 西安石油大学材料科学与工程系, 陕西西安 710065

详细信息
    作者简介:

    王静,女,1981年生,宁夏人,硕土生,主要从事石油管材腐蚀与防护方面的研究。

  • 中图分类号: TG172.6+3

CO2 Corrosion Behavior of 09Cr2AlMoRE Steel

  • 1. The Key Laboratory for Mechanical and Environment Behavior of Tubular of CNPC, Xi'an 710065, China;

  • 2. Department of Materials of Science and Engineering, Xi'an Petroleum University, Xi'an 710065, China

    摘要
  • 摘要: 为了评价新型材料09Cr2AlMoRE的CO2腐蚀性能,采用高温高压釜模拟该材料的油田CO2腐蚀环境,考察和分析了其CO2腐蚀速率、腐蚀形貌和腐蚀产物膜的化学成分。结果表明,在CO2腐蚀环境中09Cr2AlMoRE主要发生均匀腐蚀,平均腐蚀速率在0.3~1.5 mm/a;其腐蚀产物膜主要成分为FeCO3,不同温度下成分略有差异。

     

    Abstract: CO2 corrosion environment of oil field was simulated in autoclave and corrosion behavior of 09Cr2AlMoRE steel was investigated.Average corrosion rate was calculated and composition of corrosion product was analyzed.It is found that uniform corrosion is dominate,the corrosion rate is quick and the composition of the corrosion scale varies at different test temperature but FeCO3 is always the main ingrediant.The result indicates that the steel is not suitable for using in CO2 corrosion environment and a proper consideration about working environment shall be taken when it is used.

     

    • HTML全文
    • 参考文献(0)
    • 相关文章
    • 施引文献
  • 资源附件(0)
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  10
  • HTML全文浏览量:  5
  • PDF下载量:  0
  • 被引次数: 0
出版历程
  • 收稿日期:  2005-04-18
  • 网络出版日期:  2024-06-15

目录

    /

    返回文章
    返回

    版权所有 © 《材料开发与应用》编辑部豫ICP备13020589号-2

    地址：  电话：(0379)67256265;  (0379)67256345  Email：TG023@163.com

    本系统由 北京仁和汇智信息技术有限公司 开发    百度统计