铜对低碳马氏体抗菌不锈钢性能的影响

赵荣达,  王小丽,  张伟强,  朱宏飞

downloadPDF
文章导航 > 材料开发与应用  > 2006 >  21(5): 14-16
赵荣达, 王小丽, 张伟强, 朱宏飞. 铜对低碳马氏体抗菌不锈钢性能的影响[J]. 材料开发与应用, 2006, 21(5): 14-16. doi: 10.19515/j.cnki.1003-1545.2006.05.005
引用本文: 赵荣达, 王小丽, 张伟强, 朱宏飞. 铜对低碳马氏体抗菌不锈钢性能的影响[J]. 材料开发与应用, 2006, 21(5): 14-16. doi: 10.19515/j.cnki.1003-1545.2006.05.005
shu
ZHAO Rong-da, WANG Xiao-li, ZHANG Wei-qiang, ZHU Hong-fei. Influence of Cu on Properties of Low Carbon Antibacterical Martensite Stainless Steel[J]. Development and Application of Materials, 2006, 21(5): 14-16. doi: 10.19515/j.cnki.1003-1545.2006.05.005
Citation: ZHAO Rong-da, WANG Xiao-li, ZHANG Wei-qiang, ZHU Hong-fei. Influence of Cu on Properties of Low Carbon Antibacterical Martensite Stainless Steel[J]. Development and Application of Materials, 2006, 21(5): 14-16. doi: 10.19515/j.cnki.1003-1545.2006.05.005
shu

铜对低碳马氏体抗菌不锈钢性能的影响

doi: 10.19515/j.cnki.1003-1545.2006.05.005

  • 1. 辽宁工程技术大学材料科学与工程系, 辽宁 阜新 123000;

  • 2. 辽宁工程技术大学理学院, 辽宁 阜新 123000

详细信息
    作者简介:

    赵荣达,男,1981年生,辽宁海城人,硕士研究生。主要从事抗菌不锈钢的开发和研制。

  • 中图分类号: TG142.71

Influence of Cu on Properties of Low Carbon Antibacterical Martensite Stainless Steel

  • Material Science and Engineering Department, Liaoning Technical University, Fuxin 123000, China;

  • 2. Institute of Science, Liaoning Technical University, Fuxin 123000, China

    摘要
  • 摘要: 在低碳马氏体不锈钢中添加适量Cu,经过抗菌热处理,使不锈钢具有优良的抗菌特性。利用X射线衍射仪和恒电位仪分析了抗菌处理后相的分布和耐蚀性,并通过覆膜法测定其抗菌性。结果表明,随着Cu含量的增加,含铜马氏体不锈钢的硬度和抗菌性提高,维钝电流密度、致钝电流密度和致钝电压减小,更易于钝化。

     

    Abstract: A low carbon martensite stainless steel containing proper amount of Cu was prepared which exhibits antibacterial ability after antibacterial treatment.The distribution of phase and corrosion resistance and antibacterial property of the stainless steel were studied.The results show that with the increase of Cu content,hardness and antibacterial ability of the stainless steel increase and the uygur obtuse current density,the obtuse current desity and the obtuse voltage decrease indicating passivation of stainless steel is easy.

     

    • HTML全文
    • 参考文献(0)
    • 相关文章
    • 施引文献
  • 资源附件(0)
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  19
  • HTML全文浏览量:  13
  • PDF下载量:  0
  • 被引次数: 0
出版历程
  • 收稿日期:  2005-11-20
  • 网络出版日期:  2024-06-19

目录

    /

    返回文章
    返回

    版权所有 © 《材料开发与应用》编辑部豫ICP备13020589号-2

    地址：  电话：(0379)67256265;  (0379)67256345  Email：TG023@163.com

    本系统由 北京仁和汇智信息技术有限公司 开发    百度统计