低功耗NiCuZn铁氧体的研究

Study on the Low Power Loss of NiCuZn Ferrite

Institute of Material Science and Engineer,Xi’an University of Architecture and Technology,Xi’an 710055,China

摘要: 用传统陶瓷工艺制备了Ni_0.32Cu_0.10Zn_0.60O(Fe₂O₃)_0.98铁氧体材料,研究了添加V₂O₅对材料烧结特性和磁性能的影响。结果表明,当V₂O₅为0.12%(w)时,晶粒生长均匀、结构较好。此时在50kHz、150mT、100℃测试条件下,功耗有最小值(275.7 kW/m³),其值为未掺杂损耗(689.5 kW/m³)的40%。
- NiCuZn铁氧体 /
- 功耗 /
- 微观结构 /
- V₂O₅添加
Abstract: (Ni_0.32Cu_0.1Zn_0.60)O(Fe₂O₃)_0.98 ferrite was prepared by traditional ceramic process.Effects of V₂O₅ additives on the sintering behaviors and magnetic properties of NiCuZn ferrites were investigated.It was found that the minimum power loss as low as 275.7kW/m³(measured at a frequency of 50kHz,magnetic field 150mT and temperature of 100℃)for a homogeneous and fine-grained microstructure was achieved for sample with 0.12%(w) V₂O₅,decreased by 40% compared to the sample without adding V₂O₅.
- NiCuZn ferrite /
- Power loss /
- Microstructure /
- V₂O₅ addition

[1]	邵峰,朱孝平,袁兴华,等.低损耗NiCuZn铁氧体[C].中国磁性材料产业市场发展高峰论坛,深洲,2006.
[2]	M櫣rbe J,T pfer J.Ni-Cu-Zn Ferrites for lowtemperaturefiring:II.effects of powder morphology and Bi2O3additionon microstructure and permeability[J].J Electroceram,2006,16:199-205.
[3]	Jen-Yan Hsu,Wen-Song KO,Chi-Jen Chen.The effect ofV2O5on the sintering of NiCuZn ferrite[J].IEEE TransMagn,1995,31(6):3994-3996.
[4]	SeOS H,OhJ H.Effect of MoO3addition onsintering be-haviors and magnetic properties of NiCuZnferritefor multi-layer chipinductor[J].IEEE Trans Magn,1999,35(5):3412-3414.
[5]	Hui Zhong,Huai Wu Zhang,Hai Tao Zhou,et al.Effectsof WO3substitution on electromagnetic properties ofNiCuZn ferrite[J].Journal of Magnetism and MagneticMaterials,2006,300:445-450.
[6]	向兴元,张怀武.Co2O3或/和V2O5掺杂对NiZn铁氧体磁性能的影响[J].磁性材料及器件,2003,34(3):9-10.