SiO2掺杂99BeO陶瓷的微观结构与性能

唐海燕,  钟朝位,  张树人,  李志刚,  薛超,  王海蓉,  田立宏,  储齐晓

downloadPDF
文章导航 > 材料开发与应用  > 2007 >  22(6): 17-19
唐海燕, 钟朝位, 张树人, 李志刚, 薛超, 王海蓉, 田立宏, 储齐晓. SiO2掺杂99BeO陶瓷的微观结构与性能[J]. 材料开发与应用, 2007, 22(6): 17-19. doi: 10.19515/j.cnki.1003-1545.2007.06.005
引用本文: 唐海燕, 钟朝位, 张树人, 李志刚, 薛超, 王海蓉, 田立宏, 储齐晓. SiO2掺杂99BeO陶瓷的微观结构与性能[J]. 材料开发与应用, 2007, 22(6): 17-19. doi: 10.19515/j.cnki.1003-1545.2007.06.005
shu
TANG Hai-yan, ZHONG Chao-wei, ZHANG Shu-ren, LI Zhi-gang, XUE Chao, WANG Hai-rong, TIAN Li-hong, CHU Qi-xiao. Microstructure and Properties of SiO2-doped High Pure Beryllium Oxide Ceramics[J]. Development and Application of Materials, 2007, 22(6): 17-19. doi: 10.19515/j.cnki.1003-1545.2007.06.005
Citation: TANG Hai-yan, ZHONG Chao-wei, ZHANG Shu-ren, LI Zhi-gang, XUE Chao, WANG Hai-rong, TIAN Li-hong, CHU Qi-xiao. Microstructure and Properties of SiO2-doped High Pure Beryllium Oxide Ceramics[J]. Development and Application of Materials, 2007, 22(6): 17-19. doi: 10.19515/j.cnki.1003-1545.2007.06.005
shu

SiO2掺杂99BeO陶瓷的微观结构与性能

doi: 10.19515/j.cnki.1003-1545.2007.06.005

  • 1. 电子科技大学电子薄膜与集成器件重点实验室, 四川 成都 610054;

  • 2. 国营799厂, 四川 宜宾 644001

详细信息
    作者简介:

    唐海燕,男,1979年生,硕士研究生,从事高导热绝缘陶瓷材料研究

  • 中图分类号: TN604

Microstructure and Properties of SiO2-doped High Pure Beryllium Oxide Ceramics

  • 1. State Key Laboratory of Electronic Thin Films and Integrated Devices, University of Electronic Science and Technology of China, Chengdu 610054, China;

  • 2. No. 799 State-owned Factory, Yibin 644001, China

    摘要
  • 摘要: 采用固相法制备99BeO陶瓷样品,系统研究了SiO2掺杂对99BeO高导热陶瓷微观结构及性能的影响。研究发现,随着SiO2含量的增加,99BeO陶瓷的抗折强度、密度、导热率以及电学性能均呈较明显的单峰分布。当SiO2掺杂量为0.8%(w)时,可获得性能优良、结构致密的高导热陶瓷,其抗折强度为248 MPa,密度为2.957 g/cm3,导热率为303 W/(m.K)。

     

    Abstract: Effects of SiO2- content on microstructure and properties of high pure beryllium oxide high thermal conductive ceramic prepared by solid state react method were investigated.The results revealed that with the increase of SiO2 content,flexural strength,density,thermal conductivity and electric properties increases first and then slightly decreases.The sample with 0.8% SiO2(mass faction)have excellent properties and denser microstructure,with the flexural strength of 248 MPa,density of 2.957 g/cm3,the thermal conductivity of 303 W/(m·K).

     

    • HTML全文
    • 参考文献(0)
    • 相关文章
    • 施引文献
  • 资源附件(0)
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  1
  • HTML全文浏览量:  1
  • PDF下载量:  0
  • 被引次数: 0
出版历程
  • 收稿日期:  2007-04-09
  • 网络出版日期:  2024-03-30

目录

    /

    返回文章
    返回

    版权所有 © 《材料开发与应用》编辑部豫ICP备13020589号-2

    地址：  电话：(0379)67256265;  (0379)67256345  Email：TG023@163.com

    本系统由 北京仁和汇智信息技术有限公司 开发    百度统计