钢中MnS对BN析出行为的影响

尹士科,  阿荣,  谷野满

downloadPDF
文章导航 > 材料开发与应用  > 2012 >  27(2): 1-4,8
尹士科, 阿荣, 谷野满. 钢中MnS对BN析出行为的影响[J]. 材料开发与应用, 2012, 27(2): 1-4,8. doi: 10.19515/j.cnki.1003-1545.2012.02.001
引用本文: 尹士科, 阿荣, 谷野满. 钢中MnS对BN析出行为的影响[J]. 材料开发与应用, 2012, 27(2): 1-4,8. doi: 10.19515/j.cnki.1003-1545.2012.02.001
shu
YIN Shi-ke, A Rong, GU Ye-man. Effects of MnS on BN Precipitation in Steel[J]. Development and Application of Materials, 2012, 27(2): 1-4,8. doi: 10.19515/j.cnki.1003-1545.2012.02.001
Citation: YIN Shi-ke, A Rong, GU Ye-man. Effects of MnS on BN Precipitation in Steel[J]. Development and Application of Materials, 2012, 27(2): 1-4,8. doi: 10.19515/j.cnki.1003-1545.2012.02.001
shu

钢中MnS对BN析出行为的影响

doi: 10.19515/j.cnki.1003-1545.2012.02.001

  • 1. 中国钢研科技集团公司, 北京 100081;

  • 2. 新日本製铁(株)基础研究所, 川崎 211, 日本

详细信息
    作者简介:

    尹士科，男，汉族，1941年生，教授级高工，获国家科技进步二等奖2项，部级科技进步一等奖3项，获国家授权发明专利7项，出版著作和译著共14部，发表论文70余篇

  • 中图分类号: TG42

Effects of MnS on BN Precipitation in Steel

  • 1. China Iron and Steel Research Institute Group, Beijing 100081, China;

  • 2. Fundamental Research Laboratories, Nippon Steel Corporation, Kawasaki 211, Japan

    摘要
  • 摘要: 采用α粒子径迹法和电子显微镜研究了含微量硼的低碳钢中MnS对BN析出行为的影响。结果表明,当加热温度低于1150℃时,BN多以球状的MnS为结晶核心在其周围析出,呈MnS+BN复合体形态;当加热温度超过1150℃时,未固溶的MnS大部分由球形变成多面体形,这种形状的MnS已失去BN结晶核心的作用。除了呈MnS+BN复合体存在的BN外,也有单体的BN,随着温度的提高和保温时间的延长,其尺寸变大,形貌各异。

     

    Abstract: The α-particle autoradiograph and microscope were applied for studying the effects of MnS on BN precipitation in the steel containing small amount of boron. The results showed that BN nucleated on the spherical MnS and formed the compound of MnS + BN. With the increase of heating temperature over 1150 ℃ ， most of undissolved MnS particles were transformed to the shape of polyhedron， and would be ineffective for BN nucleation anymore. In addition there were also monomers of BN with different shapes formed in steel during heat treatment and their dimensions were getting larger with increase of temperature and holding time.

     

    • HTML全文
    • 参考文献(0)
    • 相关文章
    • 施引文献
  • 资源附件(0)
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  4
  • HTML全文浏览量:  3
  • PDF下载量:  0
  • 被引次数: 0
出版历程
  • 收稿日期:  2011-11-18
  • 网络出版日期:  2024-03-25

目录

    /

    返回文章
    返回

    版权所有 © 《材料开发与应用》编辑部豫ICP备13020589号-2

    地址：  电话：(0379)67256265;  (0379)67256345  Email：TG023@163.com

    本系统由 北京仁和汇智信息技术有限公司 开发    百度统计