羰基铁粉表面改性及其电磁性能研究

叶志民,  庄海燕,  董伟,  任润桃,  燕刘军

downloadPDF
文章导航 > 材料开发与应用  > 2014 >  29(6): 87-92
叶志民, 庄海燕, 董伟, 任润桃, 燕刘军. 羰基铁粉表面改性及其电磁性能研究[J]. 材料开发与应用, 2014, 29(6): 87-92. doi: 10.19515/j.cnki.1003-1545.2014.06.018
引用本文: 叶志民, 庄海燕, 董伟, 任润桃, 燕刘军. 羰基铁粉表面改性及其电磁性能研究[J]. 材料开发与应用, 2014, 29(6): 87-92. doi: 10.19515/j.cnki.1003-1545.2014.06.018
shu
YE Zhi-min, ZHUANG Hai-yan, DONG Wei, REN Run-tao, YAN Liu-jun. Study on the Electromagnetic Properties of the Surface Modified Carbonyl Iron[J]. Development and Application of Materials, 2014, 29(6): 87-92. doi: 10.19515/j.cnki.1003-1545.2014.06.018
Citation: YE Zhi-min, ZHUANG Hai-yan, DONG Wei, REN Run-tao, YAN Liu-jun. Study on the Electromagnetic Properties of the Surface Modified Carbonyl Iron[J]. Development and Application of Materials, 2014, 29(6): 87-92. doi: 10.19515/j.cnki.1003-1545.2014.06.018
shu

羰基铁粉表面改性及其电磁性能研究

doi: 10.19515/j.cnki.1003-1545.2014.06.018

  • 1. 南京理工大学 化工学院, 江苏 南京 210094;

  • 2. 海洋腐蚀与防护国防科技重点实验室, 福建 厦门 361101;

  • 3. 中国船舶重工集团公司第七二五研究所厦门材料研究院, 福建 厦门 361101

详细信息
    作者简介:

    叶志民,男,1988年生,南京理工大学硕士研究生。研究方向:应用化学。

    通讯作者:

    董伟,南京理工大学博士生导师,E-mail:dongwei@mail.njust.edu.cn。

  • 中图分类号: TM271

Study on the Electromagnetic Properties of the Surface Modified Carbonyl Iron

  • 1. Chemical Engineering Institute, Nanjing University of Science and Technology, Nanjing 210094, China;

  • 2. Science and Technology on Marine Corrosion and Protection Laboratory, Xiamen 361101, China;

  • 3. Xiamen Branch of Luoyang Ship Material Research Institute, Xiamen 361101, China

    摘要
  • 摘要: 用正硅酸乙酯(TEOS)对羰基铁颗粒进行表面改性,用扫描电镜、矢量网络分析仪等,对羰基铁在2—18 GHz范围内改性效果和影响规律进行了研究。结果表明,包覆SiO2降低了羰基铁介电常数实部,但对磁导率实部影响较小;羰基铁的电磁匹配性能得到改善。

     

    Abstract: The surface of carbonyl iron particles was modified using TEOS, the carbonyl iron modification effect within 2-18GHz and the influence rule were analyzed by the scanning electron microscopy (SEM), the vector network analyzer. The results show that coated SiO2 reduces the real component of carbonyl iron dielectric constant, but the real component magnetic permeability changes a little. The electromagnetic matching performance of carbonyl iron is improved.

     

    • HTML全文
    • 参考文献(0)
    • 相关文章
    • 施引文献
  • 资源附件(0)
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  5
  • HTML全文浏览量:  2
  • PDF下载量:  0
  • 被引次数: 0
出版历程
  • 收稿日期:  2014-07-07
  • 网络出版日期:  2024-03-22

目录

    /

    返回文章
    返回

    版权所有 © 《材料开发与应用》编辑部豫ICP备13020589号-2

    地址：  电话：(0379)67256265;  (0379)67256345  Email：TG023@163.com

    本系统由 北京仁和汇智信息技术有限公司 开发    百度统计