Nb-7Ta合金电子束真空熔炼中元素挥发动力学研究

冯益,  刘松良,  罗文忠,  赖运金,  付宝全,  冯冉,  杜建超,  何涛,  刘向宏

downloadPDF
文章导航 > 材料开发与应用  > 2015 >  30(2): 37-41
冯益, 刘松良, 罗文忠, 赖运金, 付宝全, 冯冉, 杜建超, 何涛, 刘向宏. Nb-7Ta合金电子束真空熔炼中元素挥发动力学研究[J]. 材料开发与应用, 2015, 30(2): 37-41. doi: 10.19515/j.cnki.1003-1545.2015.02.008
引用本文: 冯益, 刘松良, 罗文忠, 赖运金, 付宝全, 冯冉, 杜建超, 何涛, 刘向宏. Nb-7Ta合金电子束真空熔炼中元素挥发动力学研究[J]. 材料开发与应用, 2015, 30(2): 37-41. doi: 10.19515/j.cnki.1003-1545.2015.02.008
shu
FENG Yi, LIU Song-liang, LUO Wen-zhong, LAI Yun-jin, FU Bao-quan, FENG Ran, DU Jian-chao, HE Tao, LIU Xiang-hong. Study on Evaporation Kinetic Nb-7Ta Alloy in the EBM Vacuum Melting[J]. Development and Application of Materials, 2015, 30(2): 37-41. doi: 10.19515/j.cnki.1003-1545.2015.02.008
Citation: FENG Yi, LIU Song-liang, LUO Wen-zhong, LAI Yun-jin, FU Bao-quan, FENG Ran, DU Jian-chao, HE Tao, LIU Xiang-hong. Study on Evaporation Kinetic Nb-7Ta Alloy in the EBM Vacuum Melting[J]. Development and Application of Materials, 2015, 30(2): 37-41. doi: 10.19515/j.cnki.1003-1545.2015.02.008
shu

Nb-7Ta合金电子束真空熔炼中元素挥发动力学研究

doi: 10.19515/j.cnki.1003-1545.2015.02.008

  • 1. 西部超导材料科技股份有限公司 超导材料制备国家工程实验室, 陕西 西安 710018;

  • 2. 海军驻沈阳地区航空军事代表室, 辽宁 沈阳 110850;

  • 3. 西北工业大学材料学院, 陕西 西安 710072

基金项目: 

国家973计划项目(2008CB717903)；国家863计划项目(2009AA035401)；国际合作项目(2010DFB50280)

详细信息
    作者简介:

    冯益,男,1974年生,硕士,工程师,主要从事稀有金属熔炼和加工研究,E-mail:fengyi741120@163.com

  • 中图分类号: TG146.4

Study on Evaporation Kinetic Nb-7Ta Alloy in the EBM Vacuum Melting

  • 1. National Engineering Laboratory for Superconducting Materials, Western Superconducting Technologies Co., Ltd., Xi'an 710018, China;

  • 2. Navy Aviation Military Representative Office in Shenyang, Shenyang 110850, China;

  • 3. School of Materials, Northwestern Polytechnical University, Xi'an 710012, China

    摘要
  • 摘要: 研究了电子束熔炼Nb-7Ta合金时基体铌和杂质铁挥发过程的动力学特性。结果表明:在3 473 K时,基体铌和杂质铁挥发过程均是以单原子形式进行。铌在铌钽合金液相中扩散系数为5.78×10-7m/s,挥发反应的反应常数为1.29×10-5m/s;铁在铌钽合金液相中扩散系数为8.10×10-7m/s,挥发反应的反应常数为1.55×10-5m/s。基体铌和杂质铁挥发过程均受各自原子在液相中扩散控制。

     

    Abstract: The Evaporation kinetic characteristic of Nb-7Ta alloy in the EBM process were studied in this paper.The results show that the evaporation reaction of Nb and Fe was in the form of single atoms.The diffusion constant of Nb in the liquid Nb-7Ta alloy is 5.78 × 10-7m / s; the reaction constant of Nb in the evaporation reaction is 1.29 × 10-5m / s; the diffusion coefficient of Fe in liquid Nb-7Ta alloy is 8.10 × 10-7m / s,the reaction coefficient of Fe in the evaporation reaction is 1.55 ×10-5m / s.The evaporating process of matrix Nb as well as impurity Fe from the Nb-7Ta alloy liquid were both controlled by diffusion.

     

    • HTML全文
    • 参考文献(0)
    • 相关文章
    • 施引文献
  • 资源附件(0)
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  5
  • HTML全文浏览量:  2
  • PDF下载量:  0
  • 被引次数: 0
出版历程
  • 收稿日期:  2014-10-20
  • 网络出版日期:  2024-03-19

目录

    /

    返回文章
    返回

    版权所有 © 《材料开发与应用》编辑部豫ICP备13020589号-2

    地址：  电话：(0379)67256265;  (0379)67256345  Email：TG023@163.com

    本系统由 北京仁和汇智信息技术有限公司 开发    百度统计