压力注浆成型ITO靶材坯体的夹层现象及影响因素研究

杨硕,  王伟宁,  张大帅,  朱玉龙

downloadPDF
文章导航 > 材料开发与应用  > 2018 >  33(4): 91-99
杨硕, 王伟宁, 张大帅, 朱玉龙. 压力注浆成型ITO靶材坯体的夹层现象及影响因素研究[J]. 材料开发与应用, 2018, 33(4): 91-99. doi: 10.19515/j.cnki.1003-1545.2018.04.017
引用本文: 杨硕, 王伟宁, 张大帅, 朱玉龙. 压力注浆成型ITO靶材坯体的夹层现象及影响因素研究[J]. 材料开发与应用, 2018, 33(4): 91-99. doi: 10.19515/j.cnki.1003-1545.2018.04.017
shu
YANG Shuo, WANG Weining, ZHANG Dashuai, ZHU Yulong. Study on Factors Influencing Interlayer of ITO Green Body by Pressure Slip Casting[J]. Development and Application of Materials, 2018, 33(4): 91-99. doi: 10.19515/j.cnki.1003-1545.2018.04.017
Citation: YANG Shuo, WANG Weining, ZHANG Dashuai, ZHU Yulong. Study on Factors Influencing Interlayer of ITO Green Body by Pressure Slip Casting[J]. Development and Application of Materials, 2018, 33(4): 91-99. doi: 10.19515/j.cnki.1003-1545.2018.04.017
shu

压力注浆成型ITO靶材坯体的夹层现象及影响因素研究

doi: 10.19515/j.cnki.1003-1545.2018.04.017

  • 1. 中国船舶重工集团公司第七二五研究所, 河南 洛阳 471023;

  • 2. 大连理工大学材料科学与工程学院, 辽宁 大连 116024

基金项目: 

国家战略性新兴产业发展专项(发改办高技[2012]1029号)

详细信息
    作者简介:

    杨硕,工程师,主要从事于光电陶瓷方面的研究。E-mail:longtouys@163.com。

  • 中图分类号: TF124

Study on Factors Influencing Interlayer of ITO Green Body by Pressure Slip Casting

  • 1. Luoyang Ship Material Research Institute, Luoyang 471023, China;

  • 2. School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, China

    摘要
  • 摘要: 以ITO粉体为原料,制备出高固含量浆料,而后采用压力注浆成型获得ITO靶材坯体。研究了模具孔隙尺寸、原料粉以及助滤剂因素对坯体和靶材中间夹层表现程度的影响。结果表明,调整模具孔隙尺寸和加入助滤剂具有减轻甚至消除坯体中间夹层的作用;同时,使用烧结活性更高的原始粉制坯,可明显减轻烧结后靶材中间的夹层。

     

    Abstract: ITO green body was prepared by pressure slip casting from solid high content slurry with ITO powder as the raw material. The effects of pore-size of mould, grain-size of powder and aid-filtration reagent green body were studied. The result showed that increasing the pore-size and adding aid-filtration reagent properly could decrease or even eliminate interlayer in the green body, meanwhile, interlayer-defects in the target material could be alleviated apparently with ITO powder of high sintering activity.

     

    • HTML全文
    • 参考文献(0)
    • 相关文章
    • 施引文献
  • 资源附件(0)
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  4
  • HTML全文浏览量:  2
  • PDF下载量:  1
  • 被引次数: 0
出版历程
  • 收稿日期:  2018-02-01
  • 网络出版日期:  2024-03-18

目录

    /

    返回文章
    返回

    版权所有 © 《材料开发与应用》编辑部豫ICP备13020589号-2

    地址：  电话：(0379)67256265;  (0379)67256345  Email：TG023@163.com

    本系统由 北京仁和汇智信息技术有限公司 开发    百度统计