超低碳SiCrMn2Ni4钢连续冷却转变行为研究

陈雪龙,  王其红,  王任甫,  杨超飞,  张玉祥

downloadPDF
文章导航 > 材料开发与应用  > 2019 >  34(2): 43-48
陈雪龙, 王其红, 王任甫, 杨超飞, 张玉祥. 超低碳SiCrMn2Ni4钢连续冷却转变行为研究[J]. 材料开发与应用, 2019, 34(2): 43-48. doi: 10.19515/j.cnki.1003-1545.2019.02.007
引用本文: 陈雪龙, 王其红, 王任甫, 杨超飞, 张玉祥. 超低碳SiCrMn2Ni4钢连续冷却转变行为研究[J]. 材料开发与应用, 2019, 34(2): 43-48. doi: 10.19515/j.cnki.1003-1545.2019.02.007
shu
CHEN Xuelong, WANG Qihong, WANG Renfu, YANG Chaofei, ZHANG Yuxiang. Study on Continuous Cooling Transformation Behavior of Ultra-low Carbon SiCrMn2Ni4 Steel[J]. Development and Application of Materials, 2019, 34(2): 43-48. doi: 10.19515/j.cnki.1003-1545.2019.02.007
Citation: CHEN Xuelong, WANG Qihong, WANG Renfu, YANG Chaofei, ZHANG Yuxiang. Study on Continuous Cooling Transformation Behavior of Ultra-low Carbon SiCrMn2Ni4 Steel[J]. Development and Application of Materials, 2019, 34(2): 43-48. doi: 10.19515/j.cnki.1003-1545.2019.02.007
shu

超低碳SiCrMn2Ni4钢连续冷却转变行为研究

doi: 10.19515/j.cnki.1003-1545.2019.02.007

  • 中国船舶重工集团公司第七二五研究所, 河南 洛阳 471023

详细信息
    作者简介:

    陈雪龙,1993年生,硕士研究生,研究方向:船体钢;E-mail:chenxuelong1993@126.com。

  • 中图分类号: TG401

Study on Continuous Cooling Transformation Behavior of Ultra-low Carbon SiCrMn2Ni4 Steel

  • Luoyang Ship Material Research Institute, Luoyang 471023, China

    摘要
  • 摘要: 研究了超低碳SiCrMn2Ni4钢钢连续冷却过程, 采用金相显微镜、SEM和TEM对组织进行观察分析。结果表明, 试验钢在连续冷却后, 只存在粒状贝氏体和板条状贝氏体组织。随着冷却速度的加快, 组织逐渐由粒状贝氏体向板条状贝氏体转变, 当冷却速度增加至5℃/s时, 出现粒状贝氏体与板条状贝氏体的混合组织, 冷却速度大于等于20℃/s时, 组织全为板条状贝氏体。

     

    Abstract: The continuous cooling process of ultra-low carbon SiCrMn2Ni4 steel was simulated. Microstructure was observed and analyzed by metallographic microscope, SEM and TEM. The results showed that only granular bainite and lath bainite existed in the experimental steel after continuous cooling. With the increasing of cooling rate, granular bainite turned into lath bainite gradually. When the cooling rate increased to 5 ℃/s, a mixture of granular bainite and lath bainite appeared. When the cooling rate was no lower than 20 ℃/s, the microstructure was all lath bainite.

     

    • HTML全文
    • 参考文献(0)
    • 相关文章
    • 施引文献
  • 资源附件(0)
  • 加载中
WeChat 点击查看大图
计量
  • 文章访问数:  6
  • HTML全文浏览量:  1
  • PDF下载量:  0
  • 被引次数: 0
出版历程
  • 收稿日期:  2018-11-23
  • 网络出版日期:  2024-03-18

目录

    /

    返回文章
    返回

    版权所有 © 《材料开发与应用》编辑部豫ICP备13020589号-2

    地址：  电话：(0379)67256265;  (0379)67256345  Email：TG023@163.com

    本系统由 北京仁和汇智信息技术有限公司 开发    百度统计