Study on Preparation of High Strength Polysulfide Sealing Putty and its Bonding Property
-
摘要: 以液态聚硫橡胶为主体材料、二氧化锰为固化剂研究了不同牌号聚硫橡胶配比、二氧化锰用量对密封腻子力学性能的影响以及橡胶粘接面处理形式对密封腻子粘接性能的影响。结果显示，当不同分子量的液体聚硫橡胶以质量比30：55：15复配使用、二氧化锰用量为12份时，聚硫密封腻子具有较好的力学性能，砂带打磨结合等离子处理橡胶粘接面可以大幅度提高密封腻子的粘接强度。Abstract: Using liquid polysulfide rubber as main material and manganese dioxide as curing agent, the effects of ratios of different grades of polysulfide rubbers and manganese dioxide dosage on mechanical properties of sealing putty are studied, so is the effect of treatment form of rubber bonding surface on bonding properties of sealing putty. When the amount of manganese dioxide is 12 parts, the polysulfide sealing putty has better mechanical properties. The bonding strength of putty could be greatly improved when rubber bonding surface is ground with sand belt and treated with plasma.
-
Key words:
- polysulfide rubber /
- bonding strength /
- surface treatment
-
[1] 张洪雁, 曹寿德, 王景鹤. 高性能橡胶密封材料[M]. 北京:化学工业出版社, 2007. [2] 潘广萍. 不同硫化体系硫化的聚硫密封剂耐热空气老化性能的研究[J]. 化工新型材料, 2012, 40(7):152-154. [3] 全燕南, 吴松华. 环氧树脂对液体聚硫橡胶粘接及力学性能的影响[J]. 化学与黏合, 2019, 41(2):100-103. [4] 陈灵鸽. 耐水耐油聚硫橡胶密封腻子性能研究[J]. 材料开发与应用, 2002, 17(4):14-16. -
点击查看大图
计量
- 文章访问数: 222
- HTML全文浏览量: 86
- PDF下载量: 11
- 被引次数: 0
下载: