基于热加工图技术的10CrNi8MoV钢热加工工艺优化

Optimization of Hot Working Process for 10CrNi8MoV Steel based on Process￣ ing Map Technology

1. Representative Office of Navy in Jiang-nan Shipyard (Group) Co., Ltd., Shanghai 201913, China;
2. Luoyang Ship Material Research Institute, Luoyang 471023, China

摘要:
采用Gleeble-3500热力模拟机对10CrNi8MoV钢进行高温压缩试验,获得其在不同温度、应变速率和应变值下的流变应力值,并建立了10CrNi8MoV钢的热加工图。结果表明:10CrNi8MoV钢较合适的热变形区域有2个,分别为变形温度在1 020~1 100 ℃、应变速率为0.001~0.1 s^-1的中高温、中低应变速率区和变形温度在1 150~1 200 ℃、应变速率为3~10 s^-1的高温、高应变速率区;10CrNi8MoV钢在上述2个工艺区域发生变形时均能获得均匀细小的再结晶组织。
- 10CrNi8MoV钢 /
- 热加工图 /
- 热塑性
Abstract:
High temperature compression test is carried out on the 10CrNi8MoV steel by using Gleeble-3500 thermo-mechanical simulator. The flow stresses of the 10CrNi8MoV steel under different temperatures, strain rates and strains are obtained, and its hot process map is established. The results indicate that the 10CrNi8MoV steel has two suitable hot deformation regions, which are the medium/high temperature and medium/low strain rate (1 020-1 100 ℃ deformation temperature and 0.001-0.1 s^-1 strain rate) region, and the high temperature and high strain rate (1 150-1 200 ℃ deformation temperature and 3-10 s^-1 strain rate) region. When the 10CrNi8MoV steel deforms in the above two regions, the microstructure is uniform and fine dynamically recrystallized grains are fine.
- 10CrNi8MoV steel /
- processing map /
- thermo-plasticity

[1]	宋玉冰, 陈明, 郭彪, 等. 12Cr₂Mo1大型钢锭锻造裂纹分析与控制[J]. 锻压技术, 2021, 46(10):49-55.
[2]	李海明. S355NL钢低温冲击韧性影响因素分析[J]. 山东冶金, 2016, 38(4):35-37.
[3]	陈由红,王淑云,东赟鹏,等.300M超高强度钢锻造粗晶行为研究[J].航空材料学报,2011,31(z1):44-47.
[4]	PRASAD Y, RAO K, SASIDHAR S. Hot working gui-de:A compendium of processing maps (Second edition)[M]. Ohio:ASM International, 1997.
[5]	王艳, 王明家, 蔡大勇, 等. 高强度奥氏体不锈钢的热变形行为及其热加工图[J]. 材料热处理学报, 2005, 26(4):65-68.
[6]	权思佳, 宋克兴, 张彦敏, 等. 基于MATLAB的Ti80合金热变形行为及热加工图[J]. 稀有金属材料与工程, 2019, 48(11):3600-3607.
[7]	姚晶晶, 张迪, 张济山. 基于本构方程和热加工图的Al-xMg-2.8Zn合金的热变形行为研究[J]. 稀有金属材料与工程, 2022, 51(6):2046-2055.
[8]	袁战伟, 李付国, 王春伟, 等. 基于Murty准则的SiCp/Al复合材料热加工图研究[J]. 材料导报, 2018, 32(4):657-661.