防护涂层对固体浮力材料耐静水压性能的影响

基金项目:

国家重点研发计划项目(2021YFC2803102)

Effect of Protective Coating on Solid Buoyancy Material under Hydrostatic Pressure

State Key Laboratory of Marine Coating, Marine Chemical Research Institute Co., Ltd., Qingdao 266071, China

摘要: 潜器上的浮力材料在涂装防护涂层后,在海洋环境试验中经常会出现凹陷开裂等问题,因此对涂装不同种类涂层的浮力材料的耐全方位静水压性能进行了研究。结果表明:涂层种类对材料的影响较小;包覆涂层后,浮力材料的耐静水压性能下降,使用水深变浅;提出了表面涂装防护涂层的固体浮力材料在静水压作用下的破坏机理。
- 固体浮力材料 /
- 静水压 /
- 涂层 /
- 破坏机理
Abstract: Since buoyancy materials for submersibles often suffer from problems such as denting and cracking during the marine environmental tests after being coated with protective coatings, the all-round hydrostatic pressure resistance of buoyancy materials coated with different kinds of coatings is investigated. The results show that the type of coating has a small effect on the material. After wrapped the coating, the hydrostatic pressure resistance of the material decreases and the depth of the water used becomes shallower. The damage mechanism of the solid buoyancy materials with protective coatings under hydrostatic pressure is proposed.
- solid buoyancy material /
- hydrostatic pressure /
- coating /
- failure mechanism

[1]	何成贵, 张培志, 郭方全, 等. 全海深浮力材料发展综述[J]. 机械工程材料, 2017, 41(9):14-18.
[2]	史利利, 李瑞, 胡永玲. 国内空心玻璃微珠/环氧树脂基固体浮力材料研究进展[J]. 化学与粘合, 2020, 42(2):137-139.
[3]	陈先, 周媛, 卢伟. 固体浮力材料[M]. 北京:化学工业出版社, 2011.
[4]	赵泽华. 碳纤维增强固体浮力材料的制备以及性能探究[D]. 北京:北京化工大学, 2021.
[5]	高昂, 胡明皓, 王勇智, 等. 深海高强浮力材料的研究现状[J]. 材料导报, 2016, 30(S2):80-83.
[6]	孙春宝, 邢奕, 王啟锋. 空心玻璃微珠填充聚合物合成深海高强浮力材料[J]. 北京科技大学学报, 2006, 28(6):554-558.
[7]	刘志, 翟晓康, 梁小杰, 等. 深海用碳纤维耐压壳体表面阻水涂层的施工工艺研究[J]. 化工新型材料, 2021, 49(12):215-217.
[8]	刘志, 翟晓康, 梁小杰, 等. 超低密度全海深固体浮力材料的制备及性能研究[J]. 化工新型材料, 2023, 51(2):105-107.
[9]	梁小杰, 梁宁宁, 王庆颖, 等. 浮力材料的静水压性能研究[J]. 化工新型材料, 2020, 48(7):188-190.
[10]	卢伟, 周媛, 陈先, 等. 聚氨酯弹性体在固体浮力材料上的应用[J]. 特种橡胶制品, 2009, 30(3):64-67.