Influence of Mn/Si on Microstructure and Toughness of High Strength Steel SAW Deposited Metals

More Information
  • Received Date: April 08, 2007
  • Available Online: March 29, 2024
  • The low temperature toughness test,microstructure analysis,TEM analysis were conducted in high strength steel SAW deposited metals with different Mn/Si.The relations between microstructure,form of inclusion and low temperature toughness were investigated.The result indicates that with the change of Mn/Si in high strength steel SAW deposited metals,the low temperature toughness changes.When Mn/Si=4~8,the deposited metals toughness attained 100 J at-50℃ and when Mn/Si<4 or >8,the toughness declined.
  • Related Articles

    [1]LIU Gang, DING Penglong, GAO Zhenpeng. Influence of E36 Steel Plate Components on the Toughness of Submerged Arc Welding Joint[J]. Development and Application of Materials, 2021, 36(3): 74-77.
    [2]WANG Xiaolian, WANG Qingyun, WANG Yabin. Developing of Flux of Stainless Steel Containing Nb or Ti for Wire Electrode Submerged Arc Welding[J]. Development and Application of Materials, 2019, 34(6): 70-73. DOI: 10.19515/j.cnki.1003-1545.2019.06.014
    [3]WANG Xiaolian, WANG Qingyun. Affect of Agglomerated Flux's SiO2 Content on Slag Removal Performance of Submerged Arc Welding of Stainless Steel Containing Ti and Nb[J]. Development and Application of Materials, 2018, 33(5): 33-36. DOI: 10.19515/j.cnki.1003-1545.2018.05.006
    [4]WANG Zhiyin, KONG Hongyu. Factors Influencing Loose Specific Weight of Sintered Flux and the Solution[J]. Development and Application of Materials, 2018, 33(3): 87-89. DOI: 10.19515/j.cnki.1003-1545.2018.03.015
    [5]DING Zhenbin, WANG Xian. Analysis on Weld Pit by 705-ch Flux[J]. Development and Application of Materials, 2018, 33(3): 16-20. DOI: 10.19515/j.cnki.1003-1545.2018.03.003
    [6]WANG Xiao-lian, MA Ming-liang, WANG Qing-yun. Development of a Agglomerated Flux for Stainless Steel Submerged Arc Welding[J]. Development and Application of Materials, 2012, 27(1): 21-24. DOI: 10.19515/j.cnki.1003-1545.2012.01.005
    [7]QU Zhan-yuan. Influence of Heat Input on Low Temperature Toughness of Submerged Arc Welding Seam on Marine E36 Steel[J]. Development and Application of Materials, 2010, 25(4): 7-9. DOI: 10.19515/j.cnki.1003-1545.2010.04.002
    [8]WANG Jun-min, WANG Ming-lin. Influence of C,Cu and Cr on the Mechanical Property of SAW 10CrNiCu Steel Welds[J]. Development and Application of Materials, 2006, 21(6): 1-3. DOI: 10.19515/j.cnki.1003-1545.2006.06.001
    [9]ZHANG Ruihua, FAN Ding. Development of an Activation Flux for the GTAW of Low Carbon Steel[J]. Development and Application of Materials, 2001, 16(5): 1-3,11. DOI: 10.19515/j.cnki.1003-1545.2001.05.001
    [10]Yao Rungang, Wei Zhanjiang, Zhu Bingkun. Research and Evaluation of an Agglomerated Flux with High-basicity, Low-activity and Ultra-low Diffused Hydrogen[J]. Development and Application of Materials, 2000, 15(3): 30-32,45. DOI: 10.19515/j.cnki.1003-1545.2000.03.011

Catalog

    Article Metrics

    Article views (34) PDF downloads (2) Cited by()
    Related

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return