Research Progress in Theory and Application of “Leak Before Break”Technology

More Information
  • Received Date: April 17, 2013
  • Available Online: March 21, 2024
  • This paper deals with the present leak-before-break(LBB) theory around the world,and points out that the LBB failure assessment diagram is suitable for safety assessment and widely applied.A brief description of the application of LBB theory is presented.As for design of pressure vessels,LBB technology is still in an initial stage.Transformation of LBB assessment diagram,stability of the crack propagation and the leak rate are the problems needed to be solved for pressure vessel assessment.The paper points out the direction of LBB technology in the future.
  • Related Articles

    [1]CAI Linhong, CHEN Yuanlin, LIU Shiliang, YANG Jiongxin. Corrosion Failure Analysis of Magnesium Alloy Substrate for a Portable Equipment[J]. Development and Application of Materials, 2024, 39(5): 39-43.
    [2]WANG Yu, ZHENG Wenjian, ZHUO Min, FENG Daochen, YANG Jianguo. Analysis of Stress Corrosion Cracking in Welded Joints of Q345R High-Pressure Air Cooler[J]. Development and Application of Materials, 2023, 38(5): 86-93.
    [3]HAN Maosheng, LUO Hao, LIU Lele, ZHANG Yunhao, PAN Hengpei. Failure Analysis of Copper Alloy Globe Valve[J]. Development and Application of Materials, 2021, 36(2): 49-54.
    [4]YANG Hui, YANG Rui. Failure Analysis of Leaking of Seawater Tube in a Ship[J]. Development and Application of Materials, 2016, 31(3): 28-32. DOI: 10.19515/j.cnki.1003-1545.2016.03.006
    [5]LEI Bing, HU Sheng-nan, ZHU Xue-kang, CHEN Huan. Corrosion Evaluation of Metal Bellows Used in Shipboard[J]. Development and Application of Materials, 2015, 30(6): 81-85. DOI: 10.19515/j.cnki.1003-1545.2015.06.016
    [6]HOU Wei, DUAN Mei. Influence of Fatigue Damage on the Polythionic Acid Corrosion-resistance of Bellows[J]. Development and Application of Materials, 2011, 26(6): 48-52. DOI: 10.19515/j.cnki.1003-1545.2011.06.012
    [7]FANG Dong, CHEN Ji-zhi, YUAN Ya-min, WANG Jia-min. Failure Analysis on the Delayed Fracture of 0Cr17Ni4Cu4Nb Steel Forging[J]. Development and Application of Materials, 2007, 22(4): 44-46. DOI: 10.19515/j.cnki.1003-1545.2007.04.013
    [8]ZHANG Yu-tian, YANG Fang, QI Le-hua, GAO Jun-song, ZHANG Mao-sheng. Failure Analysis on the Inconel 625 Bellows[J]. Development and Application of Materials, 2006, 21(4): 11-15. DOI: 10.19515/j.cnki.1003-1545.2006.04.004
    [9]Gao Junsong, Song Haiping, Dong Junming. Corrosion Resistance of Bellow Materials for Catalytic Cracking Unit[J]. Development and Application of Materials, 2003, 18(5): 28-31,34. DOI: 10.19515/j.cnki.1003-1545.2003.05.008
    [10]Xu Chikun, Jia Xinmin. Corrosion and Protection of Expansion Joints in Practical Use[J]. Development and Application of Materials, 2001, 16(2): 17-20. DOI: 10.19515/j.cnki.1003-1545.2001.02.005
  • Cited by

    Periodical cited type(4)

    1. 张皓. 探讨城市集中供热管网的优化设计. 科技资讯. 2024(02): 91-93 .
    2. 张皓. 城镇供热管网泄漏原因分析及相关维护要点探究. 大众标准化. 2024(09): 114-116 .
    3. 赵菲菲. 超高压采气井口阀门腐蚀失效机理研究. 中国机械. 2023(04): 111-114 .
    4. 邱实,李东昊,胡红祥,马爱利,牛聪. 换热器波纹管的腐蚀失效原因. 腐蚀与防护. 2023(10): 106-110 .

    Other cited types(1)

Catalog

    Article Metrics

    Article views (78) PDF downloads (4) Cited by(5)
    Related

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return