Experimental Study on Crack Tip Opening Displacement(CTOD) of Continuous Casting 10CrNi3MoV Steel

More Information
  • Received Date: January 17, 2003
  • Available Online: June 14, 2024
  • CTOD test is conducted with die casting and batches of continuous casting 10CrNi3MoV steel plates and the relation between CTOD characteristic value and center line segregation is analyzed. The results show that the resistance of die casting plate to crack forepart propagation is higher than that of continuous casting plates,but to crack unstable extension,the later is no lower than the former and the line segregation will results in CTOD value falling, so the carbon content in continuous casting 10CrNi3MoV steel shall be controlled at a level no more than 0.11% or some other measures shall be adopted to decrease the segregation for good fracture toughness of the steel.
  • Related Articles

    [1]ZHANG Xinyao, LIU Yong, ZHENG Guohua, ZHANG Lijuan, ZHAO Yang, ZHA Xiaoqin. Effect of Post-weld Heat Treatment on CTOD Properties of Welded Joint of S420ML High Strength Steel[J]. Development and Application of Materials, 2020, 35(5): 1-6.
    [2]ZHANG Lijuan, ZHENG Guohua, ZHAO Yang. Uncertainty Evaluation of Fracture Toughness Critical CTOD Value for Metallic Materials[J]. Development and Application of Materials, 2016, 31(4): 36-41. DOI: 10.19515/j.cnki.1003-1545.2016.04.007
    [3]CHEN Ai-zhi, PENG Ji-xiang, XU Jia-long, YANG Shu. The Influence of Composition Segregation on the Properties in Thickness Direction of 10NiCrCu Steel Produced by Continuous Casting[J]. Development and Application of Materials, 2014, 29(4): 34-39. DOI: 10.19515/j.cnki.1003-1545.2014.04.008
    [4]XU Jia-long, PENG Ji-xiang, YANG Shu, XUE Gang. Analysis of Element Distribution Character in Thickness Direction of Continuously Cast Continuously Rolling 10CrNiCu Steel Plate[J]. Development and Application of Materials, 2014, 29(2): 32-36. DOI: 10.19515/j.cnki.1003-1545.2014.02.009
    [5]YANG Guang, XUE Gang, WANG Ren-fu, GONG Xu-hui. The Calculation of Plastic Component of CTOD Inconsideration of Crack Extension[J]. Development and Application of Materials, 2012, 27(2): 77-79. DOI: 10.19515/j.cnki.1003-1545.2012.02.018
    [6]CHEN Li-zhi, ZHANG Ya-jun. Research on Low Temperature CTOD Fracture Toughness and da/dN Properties of S355N and S355N-Z25 Structural Steel Plate[J]. Development and Application of Materials, 2011, 26(5): 42-44,48. DOI: 10.19515/j.cnki.1003-1545.2011.05.010
    [7]YANG Xiu-zhi, HUO Guang-rui, YU Sheng-fu, FU Xiu-juan. CTOD Experimental Study of Twin-wire Submerged Arc Welded Joint of High-strength Hull Steel[J]. Development and Application of Materials, 2009, 24(6): 1-5. DOI: 10.19515/j.cnki.1003-1545.2009.06.001
    [8]LIU Nian-fu. Cause and Prevention of Tensile Fracture Defect of Ship Plate[J]. Development and Application of Materials, 2009, 24(1): 26-29. DOI: 10.19515/j.cnki.1003-1545.2009.01.008
    [9]YAO Shang-wei. Effect of Center Segregation on Impact Property of Continuous Casting Steel and HAZ[J]. Development and Application of Materials, 2005, 20(2): 5-7. DOI: 10.19515/j.cnki.1003-1545.2005.02.002
    [10]Zhang Zhanling, Ni Feng, Yang Liushuan. The Solidification Simulation of Zn-Al Alloy with the Consideration of Gravitational Segregation[J]. Development and Application of Materials, 2003, 18(4): 17-20. DOI: 10.19515/j.cnki.1003-1545.2003.04.005

Catalog

    Article Metrics

    Article views (35) PDF downloads (2) Cited by()
    Related

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return