Effect of Heat Treatment on Microstructure and Mechanical Properties of TC4-DT Alloy

More Information
  • Received Date: November 12, 2008
  • Available Online: March 29, 2024
  • Effect of series heat treatment on microstructure and room temperature mechanical properties of TC4-DT alloy bar in diameter 300mm was investigated.The results show that in the microstructure of 300mm bar forged in α+β region,the grains are coarse and vague with obvious grain bindery in some field,which suggests that the big TC4-DT bars has poor uniform inforgings.The tensile properties and fracture toughness of big bars being treated after α+β double annealing can reach to Rm ≥ 825MPa,RP0.2 ≥ 750 MPa,A ≥ 8%,Z ≥ 15%;KIC(T-L) ≥ 90MPa·m½,indicating excellent match properties between strength and plasticity.The fatigue crack propagation vacuity can reach 2.833036×10-6mm/cycle and 7.294209×10-6 mm/cycle respectively after heat treated at 965℃/1h AC+550℃/6h AC and 940℃/1h AC+570℃/6h AC heat treatments.
  • Related Articles

    [1]LIU Pan, DU Mifang, ZHANG Binbin, LI Jingbin. Comments on the Revision of the Standard GB/T 4949 Chemical Analysis Methods for Sacrificial Anodes of Al-Zn-In System Alloy[J]. Development and Application of Materials, 2019, 34(5): 88-94. DOI: 10.19515/j.cnki.1003-1545.2019.05.018
    [2]LI Ruiwu, SUN Pengpeng, LI Peng, YANG Qingyun, ZHANG Yunhao, LI Yaozong. Influence of Weld Toe by TIG Dressing on the Fatigue Behavior of T-joint of Titanium Alloy[J]. Development and Application of Materials, 2017, 32(5): 41-46. DOI: 10.19515/j.cnki.1003-1545.2017.05.009
    [3]WANG Zuhua, LI Chong, XUE Gang, GONG Xuhui, ZHENG Wenjian. Influence of Welding Methods on Fatigue Properties of 10Ni5CrMoV Steel Welded Joints[J]. Development and Application of Materials, 2017, 32(3): 1-4. DOI: 10.19515/j.cnki.1003-1545.2017.03.001
    [4]LIU Zhi-ying, GUO Xiao-hui, YAN Yang-yang, WANG Nai-you. Study on Structure and Properties of Zirconium R60702 on GTAW Welding Joint[J]. Development and Application of Materials, 2014, 29(4): 25-28. DOI: 10.19515/j.cnki.1003-1545.2014.04.006
    [5]ZHANG Tian-hui, CAI Zong-shou, FU Hong-cai, YAN Pei-jun, XU Ren-ping. Weld Property of Low Carbon Bainite Crack Free Steel[J]. Development and Application of Materials, 2010, 25(2): 23-27. DOI: 10.19515/j.cnki.1003-1545.2010.02.006
    [6]ZHA Xiao-qin, SHAO Jun, ZHANG Li-juan. Review on Intergranular Corrosion Testing Methods of Stainless Steels[J]. Development and Application of Materials, 2009, 24(3): 60-65. DOI: 10.19515/j.cnki.1003-1545.2009.03.016
    [7]FAN Yu-hong, YAN Jun. Torch-Brazing of T2 Copper with 1Cr17Ni2 Stainless Steel[J]. Development and Application of Materials, 2009, 24(3): 42-45. DOI: 10.19515/j.cnki.1003-1545.2009.03.012
    [8]Ma Jianmin, ‚Li Jingyong. Effect of Weld Defects on the Fatigue of Aluminum Alloy Joint[J]. Development and Application of Materials, 2003, 18(6): 31-34. DOI: 10.19515/j.cnki.1003-1545.2003.06.009
    [9]Wang Yonghua, Yang Bo. The Antiseptic Testing Methods of Nano-structure Material against Microorganism[J]. Development and Application of Materials, 2001, 16(1): 30-32. DOI: 10.19515/j.cnki.1003-1545.2001.01.008
    [10]Ma Jianpo, Ji Jialong, Li Gang. Influence of TIG Weld Dressing on Drop-weight Test Result of T-joints[J]. Development and Application of Materials, 2000, 15(3): 37-39. DOI: 10.19515/j.cnki.1003-1545.2000.03.013

Catalog

    Article Metrics

    Article views (42) PDF downloads (7) Cited by()
    Related

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return